    Super fast-cure series EVA film

    Su406&Su806


    Product introduction

    F?RST? Su406 & Su806 EVA is a super fast-cure type encapsulant product. The lamination time can be decreased to 10min~12min when modules are encapsulated using Su406/Su806 EVA. While the PV module productivity can be greatly increased with Su406 & Su806 EVA, excellent durability, as well as PID and snail trails resistance will be exhibited.


    Crosslinking Property


    Performance parameter

    Properties Test Method Units Su406 Su806
    General gram weight FST Method g/m2 430±20 390±20
    Thickness  FST Method mm 0.55±0.05 0.50±0.05
    Length FST Method m/roll 150 150
    Width FST Method mm Customization0/+7 Customization0/+7
    Density ASTMD792 g/cm3 0.95-0.96 0.95-0.96
    Melting range FST Method 40-80 40-80
    Shrinkage Rate(120,3min) GB/T29848 MD% <3.0 <3.0
    TD% <1.5 <1.5
    UV-Cutoff Wavelength FST Method nm -- 360
    Transmittance 1100nm-380nm GB/T29848 % >91 >91
    380nm-290nm % >80 <30
    Gel content GB/T29848 Gel% >75 >75
    Volume Resistivity GB/T29848 Ω·cm >1.0×1015 >1.0×1015
    Strength of Peeling from Glass GB/T29848 N/cm >60 >60
    Strength of Peeling from TPT GB/T29848 N/cm >40 >40
    Note: The gram weight, thickness, length and width of product can be customized.

    嘘禁止想象,国产大陆AV片在线观看,极品少妇第一次高潮哇哇叫
  • <menu id="yw2uu"><table id="yw2uu"></table></menu><xmp id="yw2uu"><noscript id="yw2uu"></noscript>
    <blockquote id="yw2uu"><center id="yw2uu"></center></blockquote>
    <td id="yw2uu"></td>
  • <xmp id="yw2uu">
    <noscript id="yw2uu"></noscript>