ENLIGHT series PO film
4015 & XUS66250
Product introduction
ENLIGHTTM series PO is the longest history thermoplastic polyolefin film in PV, with the characteristics of strong adherence to glass, bubble-free during lamination, no residue peroxide, makes it very suitable to encapsulate thin film modules, c-Si modules, as well as flexible modules.
Performance parameter
Properties | Test Method | Units | ENLIGHTTM4015 | ENLIGHTTMXUS66250 |
General gram weight | FST Method | g/m2 | 400±20 | 400±20 |
Thickness | FST Method | mm | 0.50±0.05 | 0.50±0.05 |
Length | FST Method | m/roll | 110 | 110 |
Width | FST Method | mm |
Customization
0/+7
|
Customization
0/+7
|
Density | ASTMD792 | g/cm3 | 0.88±0.05 | 0.88±0.05 |
Melting range | FST Method | ℃ | 40-107 | 40-105 |
Shrinkage Rate (120℃,3min) | GB/T29848 | MD% | <2.0 | <4.0 |
TD% | <1.0 | <3.0 | ||
UV-Cutoff Wavelength | FST Method | nm | -- | 360 |
Transmittance(1100nm-400nm) | GB/T29848 | % | >85 | >85 |
Volume Resistivity | ASTM/D527 | Ω·cm | ≥1.0×1015 | ≥1.0×1014 |
WVTR | ASTM F1249 | g/m2.24h | <5.0 | <5.0 |
Strength of Peeling from Glass | GB/T29848 | N/cm | >60 | >60 |
Strength of Peeling from TPT | GB/T29848 | N/cm | >40 | >40 |
?Trademark of Rohm and Haas Electronic Materials LLC.
XUR150
Product introduction
XUR150 PO is non-crosslinking polyolefin encapsulant with excellent reliability for PV modules, which can be laminated at the temperature lower than 120℃. Thus it is very suitable for perovskite cells.
Technical specifications
Note:-GB: Standardization of P. R. China
-FST Method: Enterprise standard system of P. R. China
Performance parameter
Properties |
Test method |
Unit |
XUR150 |
General gram weight |
FST Method |
g/m2 |
400±20 |
General Thickness |
FST Method |
mm |
0.50±0.05 |
General Length |
FST Method |
m/roll |
110 |
General Width |
FST Method |
mm |
Customization 0/+7 |
Density |
ASTMD792 |
g/cm3 |
0.88±0.05 |
Melting range |
FST Method |
℃ |
40-107 |
Shrinkage Rate (120℃,3min) |
GB/T29848 |
MD% |
<3.0 |
TD% |
<2.0 |
||
UV-Cutoff Wavelength |
FST Method |
nm |
- |
Transmittance(1100nm-400nm) |
GB/T29848 |
% |
>85 |
Volume Resistivity |
ASTM/D527 |
Ω·cm |
≥1.0×1015 |
WVTR |
ASTM F1249 |
g/m2.24h |
<5.0 |
Strength of Peeling from Glass |
GB/T29848 |
N/cm |
>60 |
Strength of Peeling from TPT |
GB/T29848 |
N/cm |
>40 |